The production process flow of lightly burned magnesium powder

2023-11-28 14:24:21
order

Light burned magnesium oxide powder is produced by roasting magnesite at a temperature below 1000 ℃. Light burned magnesium powder plays a role in industries such as metallurgy, chemical industry, light industry, agriculture, mining, etc. Light burned magnesium oxide is an important component of the raw materials required for the production of magnesite products, which is the active magnesium oxide produced by calcining magnesite. The ability of magnesium oxide to undergo physical adsorption and chemical reactions is known as its activity, which has a significant impact on the production process and quality of the product. Use a two-step calcination method to calcine lightly burned magnesium oxide to obtain sintered magnesia sand. Desulfurized magnesium oxide


Light burned magnesium oxide is commonly known as light burned powder, light burned magnesium oxide, and also known as caustic magnesium oxide, often presented in white and light yellow shapes. Its melting and boiling points are 2852 ℃ and 3600 ℃, respectively. It is easily soluble in acids and ammonium salts, but not easily soluble in solvents such as ethanol. It is a hard bonding material that is easily deliquescent in the air. Samples with a mass fraction higher than 98% are called high-purity magnesium oxide, which is widely used in electronics, ceramics, chemical industry, and other fields due to its excellent alkali resistance, edge resistance, light transmittance, large coefficient of thermal expansion, and excellent thermal conductivity in high-temperature environments.


At present, the production of light burned magnesium oxide is mostly achieved by calcining magnesite with a block size of 20-100mm at 700-1200 ℃. Due to differences in the decomposition rate of MgCO3 and the developmental state of MgO, there may also be differences in activity. Its activity depends on the content of active magnesium oxide in lightly burned magnesium oxide, and its physical adsorption and chemical reactivity depend on this. Therefore, the ability to accurately measure its activity directly affects the production and application of light burned magnesium oxide in practice.